Multiferroic properties of BiFeO3 /CoFe2 O4 multilayers structure at room temperature
DOI:
https://doi.org/10.18050/RevUcv-Scientia.v9n2a4Keywords:
Propiedades multiferroicas, Estructura de multicapas, Respuestas ferromagnéticas, FerroeléctricasAbstract
BiFeO3 /CoFe2 O4 multilayer films were deposited by spin coating on Pt (Pt/TiO2/SiO2/Si) substrates and 3 2 4 annealed at 700, 725 and 750 °C. The precursor of BiFeO /CoFe O for multilayers structure was 3 2 4 synthesized by chemical solution method. Patterns x-ray diffraction of the multilayers system revealed the composite-like structure. The leakage current was found less than Amp at electric field below 100 -6 10 kV/cm, which it shows the ohmic behavior of BiFeO /CoFe O . Dielectric constant decreases with increasing 3 2 4 in the frequency range 103-106 Hz. BiFeO /CoFe O system shows the co-existence of ferroelectric 3 2 4 polarization (Pr) = 65 and 51 µC/cm2 and magnetization (Mr) =102 and 47 emu/cm3 at room temperature. Observed ferromagnetic and ferroelectric responses in multilayers system may be useful for bi-functional devices.
Downloads
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
- Share — copy and redistribute the material in any medium or format
- Adapt — remix, transform, and build upon the material.
- The licensor cannot revoke these freedoms as long as you follow the license terms.
Under the following terms:
-
Attribution — You must give appropriate credit, provide a link to the license, and indicate if changes were made. You may do so in any reasonable manner, but not in any way that suggests the licensor endorses you or your use.
- No additional restrictions — You may not apply legal terms or technological measures that legally restrict others from doing anything the license permits.